Effect of brazing temperature on microstructure and mechanical properties of CMSX-4 single crystal superalloy brazed joint
-
摘要: 采用一种镍基合金钎料钎焊CMSX-4单晶高温合金，利用扫描电镜、电子探针等分析手段研究接头的微观组织与相组成，并利用高温持久试验机测试接头的高温持久性能，讨论不同钎焊工艺条件下，接头的组织与性能变化规律及接头的断裂机制。研究发现，随着钎焊温度的提高，焊缝中低熔点化合物相减少，小尺寸凝固缺陷消失，白色硼化物比例先升高后降低，γ'沉淀相增多，接头的高温组织稳定性增加。当钎焊温度不低于1 290 ℃时，CMSX-4单晶高温合金接头在980 ℃/100 MPa条件下的持久寿命可达到400 h。观察接头的断口形貌发现，断裂均发生在焊缝处，断裂模式为以脆性断裂为主的混合断裂。Abstract: The single crystal superalloy CMSX-4 was brazed with a Ni-based filler alloy,the microstructure and the phase composition were studied by scanning electron microscopy（ SEM）,electron probe microanalysis（ EPMA）. The stress rupture property of joint was tested by high temperature stress rupture property testing machine. The result shows that the fracture mechanism and stress rupture property at high temperature of joint transformed with the different brazing temperature. With the increase of brazing temperature,the low melting point eutectic phase and the solidification defect with small size disappears,the proportion of white boron compounds increases firstly and then decreases. Besides,the amount of the precipitated phase and the high temperature structure stability of joint increase. When the brazing temperature is not lower than1 290 ℃,the rupture life of CMSX-4 superalloy under the condition of 980 ℃/100 MPa reaches up to 400 h. The fracture morphology of joints shows that all the fractures occurred at the weld seam. The fracture mode of joint is the mixed fracture characterized by brittle fracture.
-
Keywords:
- single crystal superalloy /
- brazing /
- stress rupture property /
- Ni-based filler alloy
-
-
[1] 郁峥嵘, 丁贤飞, 曹腊梅, 等. 第二、三代镍基单晶高温合金含Hf过渡液相连接[J]. 金属学报, 2016, 52(5): 549-560. [2] Zhong M L, Sun H Q, Liu W J, et al. Boundary liquation and interface cracking characterization in laser deposition of Inconel 738 on directionally solidified Ni-based superalloy[J]. Scripta Materialia, 2005, 53(2): 159-164.
[3] 孙鸿卿, 钟敏霖, 刘文今, 等. 定向凝固镍基高温合金上激光熔覆Inconel 738的裂纹敏感性研究[J]. 航空材料学报, 2005, 25(2):26-31. [4] 关桥. 发动机叶片与部件修复工程中的焊接技术(上)[J]. 航空工艺技术, 1993(2): 2-12. [5] Lingenfelter A C. Welding metallurgy of nickel alloys in gas turbine components[C]. Proceedings from Materials Solutions’97 on Joining and Repair of Gas Turbine Components.New York, USA, 1997: 3-6.
[6] Henderson M B, Arrell D, Larsson R, et al. Nickel based superalloy welding practices for industrial gas turbine applications[J]. Science and Technology of Welding and Joining, 2004, 9(1): 13-21.
[7] 孙妍, 张杰, 刘春凤. BNi68CrWB钎焊K24/GH648异种高温合金的界面形成机理[J]. 焊接学报, 2017, 38(6):61-64. [8] Neumeier S, Dinkel M, Pyczak F, et al. Nanoindentation and XRD investigations of single crystalline Ni-Ge brazed nickel-base superalloys PWA 1483 and René N5[J]. Materials Science & Engineering A, 2011, 528(3): 815-822.
[9] 程建平, 张红梅. INCO718高温合金钎焊工艺研究[J]. 真空, 2010, 47(3): 31-34. [10] 孙元, 侯星宇, 金涛, 等. DD5单晶高温合金钎焊接头的微观组织和力学性能分析[J]. 焊接学报, 2017, 38(1): 117-120. [11] 李晓红, 熊华平, 张学军.先进航空材料焊接技术[M]. 北京: 国防工业出版社, 2012. [12] Nishimoto K, Saida K, Kim D, et al. Homogenization bahavior of alloying elements during transient liquid phase bonding: transient liquid phase bonding of Ni-Base single crystal superalloy (Report 4)[J]. Quarterly Journal of the Japan Welding Society, 1997, 15(3): 509-514.
[13] 李晓红, 毛唯, 郭万林, 等. DD6单晶合金过渡液相扩散焊工艺[J]. 焊接学报, 2005, 26(4): 51-54. [14] 柴禄, 侯金保, 张胜. 工艺参数对IC10单晶TLP接头组织和性能的影响[J]. 焊接学报, 39(8): 114-118. [15] Miglietti W, Pennefather R C. The microstructure, mechanical properties and coatability of diffusion brazed CMSX-4 single crystal[C]. Proceedings from Materials Solutions’ 97 on Joining and Repair of Gas Turbine Components.Materials Park, Ohio, US, 1996: 61-77.
[16] Broomfield R, Plc R R. Development of brazing techniques for the joining of single crystal components[C]. Fifth International Charles Parsons Turbine Conference, Cambridge, UK, 2000: 741-754.
[17] Maleki V, Omidvar H, Rahimipour M R. Effect of gap size on microstructure of transient liquid phase bonded IN-738LC superalloy[J]. Transactions of Nonferrous Metals Society of China, 2016, 26(2): 437-447.
[18] 关洪魏, 李文, 刘纪德. 工艺参数对一种镍基单晶高温合金TLP接头组织的影响[J]. 沈阳理工大学学报, 2017, 6(5): 84-89. [19] 孙元, 刘纪德, 侯星宇, 等. DD5单晶高温合金大间隙钎焊的组织演变与界面形成机制[J]. 金属学报, 2016, 52(7): 875-882. [20] Gale W F, Wallach E R. Microstructural development in transient liquid-phase bonding[J]. Metallurgical Transactions A, 1991, 22 (10): 2451-2457.
[21] 吴娜, 李亚江, 王娟. Super-Ni/NiCr叠层材料Ni-Cr-Si-B高温钎焊接头的组织特征及抗剪强度[J]. 焊接学报, 2014, 35(1): 9-12. [22] 于治水, 石昆, 言智, 等. 钎缝间隙对316L不锈钢真空钎焊接头组织的影响[J]. 材料工程, 2010, 22 (10): 77-81. [23] 潘林, 邢丽, 刘奋成, 等. FGH97高温合金TLP焊接接头组织分析[J]. 焊接学报, 2013, 34(4): 89-92. -
期刊类型引用(9)
1. 贺彤，王诗洋，李可馨，侯星宇，孙元. 混合钎料对镍基单晶高温合金大间隙钎焊接头组织和性能的影响. 焊接. 2024(06): 1-8 . 
本站查看
2. 贺文燮，张元伟，任海水，任新宇，毛唯. DD26单晶高温合金钎焊接头微观组织与力学性能研究. 航空制造技术. 2024(10): 102-106+114 . 百度学术
3. 周标，王浩，任新宇，邱嘉玉，潘晖. 采用BNi-5钎料钎焊K417G高温合金的界面组织和力学性能. 焊接. 2023(12): 12-16 . 本站查看
4. 王浩，吴欣，程耀永，毛唯. K480镍基高温合金钎焊接头组织与性能. 焊接. 2022(04): 37-42+47 . 本站查看
5. 纪朝辉，李旭康，孙宇博. 镍基合金钎焊连接技术研究进展. 兵器材料科学与工程. 2021(05): 135-140 . 百度学术
6. 李可馨，侯星宇，王诗洋，孙元，陈立佳，程陆凡，王振江，李寒松，汤广全. 第三代镍基单晶高温合金大间隙钎焊接头的微观组织和力学性能. 航空材料学报. 2021(05): 78-85 . 百度学术
7. 柴廷玺，徐宏彤，王希靖，张亮亮，晏丽琴. 穿孔型等离子弧自熔焊工艺对N6镍合金焊缝成形及性能的影响. 焊接. 2021(08): 29-36+63 . 本站查看
8. 赵旭，孙元，侯星宇，张洪宇，周亦胄，丁雨田. 取向偏差对镍基单晶高温合金钎焊接头组织与力学性能的影响. 金属学报. 2020(02): 171-181 . 百度学术
9. 孙元，赵旭，苏瑾，侯星宇，王诗洋，丁雨田. 镍基单晶高温合金钎焊接头的微观组织与性能. 焊接学报. 2020(07): 32-38+98-99 . 百度学术
其他类型引用(3)
计量
- 文章访问数: 528
- HTML全文浏览量: 10
- PDF下载量: 29
- 被引次数: 12
下载: