铝合金激光-TIG复合焊热输入对组织及性能的影响

马国龙, 雷振, 马寅, 徐良, 韩晓辉

马国龙, 雷振, 马寅, 徐良, 韩晓辉. 铝合金激光-TIG复合焊热输入对组织及性能的影响[J]. 焊接, 2019, (12): 7-10. DOI: 10.12073/j.hj.20190620003
引用本文: 马国龙, 雷振, 马寅, 徐良, 韩晓辉. 铝合金激光-TIG复合焊热输入对组织及性能的影响[J]. 焊接, 2019, (12): 7-10. DOI: 10.12073/j.hj.20190620003
MA Guolong, LEI Zhen, MA Yin, XU Liang, HAN Xiaohui. Effect of heat input on microstructure and properties of aluminum alloy with laser-TIG hybrid welding[J]. WELDING & JOINING, 2019, (12): 7-10. DOI: 10.12073/j.hj.20190620003
Citation: MA Guolong, LEI Zhen, MA Yin, XU Liang, HAN Xiaohui. Effect of heat input on microstructure and properties of aluminum alloy with laser-TIG hybrid welding[J]. WELDING & JOINING, 2019, (12): 7-10. DOI: 10.12073/j.hj.20190620003

铝合金激光-TIG复合焊热输入对组织及性能的影响

详细信息
    作者简介:

    马国龙,1987年出生,博士,工程师;主要从事激光焊接及激光电弧复合焊接物理机制及工艺等开发研究;已发表论文10篇.

    通讯作者:

    雷振,1981年出生,博士研究生,高级工程师

  • 中图分类号: TG456.7

Effect of heat input on microstructure and properties of aluminum alloy with laser-TIG hybrid welding

  • 摘要: 研究了激光-TIG复合焊在不同热输入下焊缝成形、接头拉伸性能、断口特征、接头硬度特征及接头金相特征。试验结果表明,在文中试验条件下:+7 mm离焦量的热输入是+5 mm离焦量的1.6倍,大热输入下,焊缝变得宽大;+7 mm离焦量下焊缝背面宽度是+5 mm离焦量的1.2倍,接头拉伸性能下降,+5 mm离焦量和+7 mm离焦量下抗拉强度分别为母材的88%和82%,断后伸长率分别为母材的96%和48%;大热输入下,断口处韧窝较为平浅,显微硬度降低;热输入较小时,无论是焊缝还是熔合区,第二相析出质点数量多而细小而且呈弥散分布;热输入较大时,焊缝及熔合区的第二相质点数量较少且尺寸较大,即焊缝及熔合区的第二相质点聚集长大。
    Abstract: Weld forming,tensile properties,fracture characteristics,hardness characteristics and microstructure characteristics of joints were studied under different heat inputs by laser-arc hybrid welding. The results showed that,under conditions of the experiment,the heat input of+ 7 mm defocus was 1. 6 times as much as that of + 5 mm defocus,and welds became wide under high heat input. The back width of welds under + 7 mm defocus was 1. 2 times that of welds under + 5 mm defocus. Tensile properties of joints decreased,tensile strength of + 5 mm defocus and + 7 mm defocus was 88% and 82% of the base metal respectively,and elongation after fracture was 96% and 48% of the base metal respectively. Under high heat input,dimples at the fracture were relatively shallow and microhardness decreased. Precipitated particles in weld and fusion zone were more,fine and dispersed under lower heat input,while they were less and coarse under higher heat input,namely they gathered and grew up.
  • [1] 雷正龙,李颖,陈彦宾,等.双光束激光填丝焊工艺对铝合金焊接气孔率的影响[J].焊接学报,2013,34(2):40-44.
    [2] 杨海锋.铝合金高功率双光束激光及与TIG复合焊接特性研究[D].哈尔滨:哈尔滨焊接研究所,2016.
    [3] 杨海锋,梁小梅,王吉孝,等.5A06铝合金激光-TIG电弧复合填丝焊的特性[J].焊接,2016(6):30-34.
    [4]

    Harooni M,Carlson B,Kovacevic R.Dual-beam laser welding of AZ31B magnesium alloy in zero-gap lap joint configuration[J].Optics and Laser Technology,2014,56:247 -255.

    [5] 夏佩云,夏令,余海松,等.6061铝合金激光填丝焊接接头组织与性能[J].焊接,2018(6):51-54.
    [6] 张亚亮,刘佳,石岩,等.电流/电压匹配对铝合金激光-TIG复合焊接过程稳定性的影响[J].焊接学报,2018,39(1):79-83.
    [7] 杨大伟,陈树海,黄继华,等.6005A铝合金激光-TIG复合热源填丝焊接技术[J].焊接学报,2017,38(10):51-54.
    [8] 黄瑞生,杨海锋,王君宇,等.铝合金双光束/单光束激光-TIG复合焊[J].焊接,2017(1):39-42.
    [9] 杨海锋,黄瑞生,常云峰,等.双光束激光-TIG复合焊电弧特性分析[J].焊接,2016(12):41-45.
  • 期刊类型引用(2)

    1. 王柏霖. 铝合金焊接工艺在动车组的应用综述. 铝加工. 2023(04): 9-13 . 百度学术
    2. 吴雁,李朝阳,郭立新,肖礼军,孙士学. 焊接工艺参数对铝/铝激光焊焊缝形貌及力学性能的影响. 焊接. 2021(11): 27-30+47+62-63 . 本站查看

    其他类型引用(4)

计量
  • 文章访问数:  40
  • HTML全文浏览量:  23
  • PDF下载量:  25
  • 被引次数: 6
出版历程
  • 收稿日期:  2019-06-19

目录

    /

    返回文章
    返回