ZHU Haishan, XU Lianyong, CAO Jian, JIA Lusheng. Effect of t8/5on fracture toughness of CGHAZ of X100 pipeline steel[J]. WELDING & JOINING, 2021, (3): 5-12. DOI: 10.12073/j.hj.20201106002
Citation: ZHU Haishan, XU Lianyong, CAO Jian, JIA Lusheng. Effect of t8/5on fracture toughness of CGHAZ of X100 pipeline steel[J]. WELDING & JOINING, 2021, (3): 5-12. DOI: 10.12073/j.hj.20201106002

Effect of t8/5on fracture toughness of CGHAZ of X100 pipeline steel

  • According to BS 7448 standard and microscopic analysis method, thermal simulation technique was used to study the fracture toughness (CTOD) of the coarse grain zone in heat affected zone of X100 grade pipeline steel under different t8/5. The results showed that CTOD value increased as the t8/5 time increased, and microstructure was transformed from lath bainite to granular bainite. The coarse chain M-A component appeared at the grain boundary of the prior austenite att8/5= 40 s, which caused a small decrease in fracture toughness. Whent8/5 was 50 s, the fracture toughness continued to increase. However, the grains tended to coarsen as t8/5 increased.
  • loading

Catalog

    Turn off MathJax
    Article Contents

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return